Gadolinium sī 1 ê hoà-ha̍k goân-sò͘. I ê goân-chú-hoan sī 64, hoà-ha̍k hû-hō sī Gd.
Gadolinium, 64Gd
![](http://178.128.105.246/cars-http-upload.wikimedia.org/wikipedia/commons/thumb/d/d1/Gadolinium-4.jpg/220px-Gadolinium-4.jpg) |
Ki-pún sèng-chit |
---|
Miâ, hû-hō |
gadolinium, Gd |
---|
Gōa-hêng |
silvery white |
---|
Gadolinium tī chiu-kî-piáu lāi ê ūi-tì |
---|
|
Goân-chú-hoan |
64 |
---|
Goân-chú-liōng (±) |
157.25(3)[1] |
---|
Goân-sò͘ lūi-pia̍t |
lanthanum-hē |
---|
Cho̍k, hun-khu |
n/a, f khu |
---|
Chiu-kî |
tē 6 chiu-kî |
---|
Tiān-chú pâi-lia̍t |
[Xe] 4f7 5d1 6s2 |
---|
per shell |
2, 8, 18, 25, 9, 2 |
---|
Bu̍t-lí sèng-chit |
---|
Siòng |
solid |
---|
Iûⁿ-tiám |
1585 K (1312 °C, 2394 °F) |
---|
Hut-tiám |
3273 K (3000 °C, 5432 °F) |
---|
Bi̍t-tō͘ (sek-un) |
7.90 g·cm−3 |
---|
7.4 g·cm−3 |
Iûⁿ-hoà-jia̍t |
10.05 kJ·mol−1 |
---|
Cheng-hoat-jia̍t |
301.3 kJ·mol−1 |
---|
Jia̍t-iông-liōng |
37.03 J·mol−1·K−1 |
---|
cheng-khì-ap (calculated)
P (Pa)
|
1
|
10
|
100
|
1 k
|
10 k
|
100 k
|
tī T (K)
|
1836
|
2028
|
2267
|
2573
|
2976
|
3535
| |
Goân-chú sèng-chit |
---|
Sng-hòa-sò͘ |
1, 2, 3 (a mildly basic oxide) |
---|
Tiān-hū-tō͘ |
Pauling scale: 1.20 |
---|
Tiān-lī-lêng |
1st: 593.4 kJ·mol−1 2nd: 1170 kJ·mol−1 3rd: 1990 kJ·mol−1 |
---|
Goân-chú pòaⁿ-kèng |
empirical: 180 pm |
---|
Kiōng-kè pòaⁿ-kèng |
196±6 pm |
---|
Cha̍p-lio̍k |
---|
Chiⁿ-thé kò͘-chō |
hexagonal close-packed (hcp) |
---|
Siaⁿ-sok (sòe kùn-á) |
2680 m·s−1 (at 20 °C) |
---|
Jia̍t-phòng-tiòng |
α poly: 9.4 µm·m−1·K−1 (at 100 °C) |
---|
Jia̍t-thoân-tō-lu̍t |
10.6 W·m−1·K−1 |
---|
Tiān-chó͘-lu̍t |
α, poly: 1.310 µΩ·m |
---|
Chû-sèng |
ferromagnetic-paramagnetic transition at 293.4 K |
---|
Young hē-sò͘ |
α form: 54.8 GPa |
---|
Shear hē-sò͘ |
α form: 21.8 GPa |
---|
Bulk hē-sò͘ |
α form: 37.9 GPa |
---|
Poisson pí |
α form: 0.259 |
---|
Vickers ngē-tō͘ |
510–950 MPa |
---|
CAS teng-kì pian-hō |
7440-54-2 |
---|
Le̍k-sú |
---|
Hō-miâ |
after the mineral Gadolinite (itself named after Johan Gadolin) |
---|
Hoat-hiān |
Jean Charles Galissard de Marignac (1880) |
---|
Siōng chá hû-lî |
Lecoq de Boisbaudran (1886) |
---|
Chòe ún-tēng ê tông-ūi-sò͘ |
---|
Chú bûn-chiong: gadolinium ê tông-ūi-sò͘ |
iso
|
NA
|
half-life
|
DM
|
DE (MeV)
|
DP
|
152Gd
|
0.20%
|
1.08×1014 y
|
α
|
2.205
|
148Sm
|
154Gd
|
2.18%
|
–
|
(α)
|
0.0812
|
150Sm
|
155Gd
|
14.80%
|
–
|
(α)
|
0.0812
|
151Sm
|
156Gd
|
20.47%
|
–
|
(SF)
|
<71.541
|
|
157Gd
|
15.65%
|
–
|
(SF)
|
<70.531
|
|
158Gd
|
24.84%
|
–
|
(SF)
|
<70.965
|
|
160Gd
|
21.86%
|
>1.3×1021 y
|
(β−β−)
|
1.729
|
160Dy
| |
Decay modes in parentheses are predicted, but have not yet been observed |